Pglass (%) | Tc = 92˚C | Tc = 98˚C | Tc = 102˚C | ||||||
n | K (s−1) | t1/2 (min) | n | K (s−1) | t1/2 (min) | n | K (s−1) | t1/2 (min) | |
Pglass-GAL | |||||||||
0 | 2.32 | 0.435 | 1.92 | 1.90 | 0.175 | 4.35 | 1.62 | 0.072 | 9.56 |
1 | 3.29 | 0.431 | 1.90 | 1.88 | 0.181 | 4.29 | 1.58 | 0.069 | 10.45 |
10 | 3.35 | 0.448 | 1.85 | 1.79 | 0.177 | 3.86 | 1.65 | 0.102 | 8.63 |
25 | 2.24 | 0.418 | 1.96 | 1.84 | 0.220 | 3.58 | 2.06 | 0.105 | 7.54 |
40 | 2.16 | 0.456 | 1.86 | 1.44 | 0.193 | 3.84 | 2.126 | 0.142 | 6.65 |
Pglass-GAH | |||||||||
0 | 2.42 | 0.425 | 1.82 | 1.80 | 0.165 | 4.25 | 1.64 | 0.082 | 9.56 |
1 | 2.24 | 0.418 | 1.96 | 1.84 | 0.220 | 3.58 | 2.06 | 0.105 | 7.54 |
10 | 2.32 | 0.435 | 1.92 | 1.90 | 0.175 | 4.35 | 1.62 | 0.072 | 10.56 |
25 | 3.29 | 0.431 | 1.90 | 1.88 | 0.181 | 4.29 | 1.58 | 0.069 | 10.45 |
40 | 3.35 | 0.448 | 1.85 | 1.79 | 0.177 | 3.86 | 1.65 | 0.102 | 8.63 |